Categories
New products
-
Standard Spiral Wound Gasket
Kaxite® Standard Spiral Wound Gasket here,Manufacture Standard Spiral Wound Gasket,Standard Spiral Wound Gasket for you, high quality and reasonable price.
-
Lens Ring Joint Gasket
Kaxite® Lens Ring Joint Gasket here,Manufacture Lens Ring Joint Gasket,Lens Ring Joint Gasket for you, high quality and reasonable price.
-
Double Jacket Gasket
Kaxite® Double Jacket Gasket here,Manufacture Double Jacket Gasket,Double Jacket Gasket for you, high quality and reasonable price.
-
Corrugated Gaskets
Kaxite® Corrugated Gaskets here,Manufacture Corrugated Gaskets,Corrugated Gaskets for you, high quality and reasonable price.
-
PTFE Envelope Gasket
Kaxite® PTFE Envelope Gasket here,Manufacture PTFE Envelope Gasket,PTFE Envelope Gasket for you, high quality and reasonable price.
Graphite Packing with Carbon Fiber Corners
Graphite packing with carbon fiber corners is a multi-fiber packing, braided from expanded graphite yarns and carbon fibers, the diagonally braided from graphite yarn, reinforced in all four corners with carbon fibers. The corners and body make the packing three times more resistant to extrusion and increase the pressure handing capabilities compared to traditional graphite packings.
Kaxite P403I
There are multi inconel wires reinforced to create the packing with increased extrusion resistance capability.
Typical Application
> It can be used in many demanding applications, both dynamic and static
> Particularly suited for high temperature and high pressure service in valves, pumps, expansion joints, mixers and agitators of pulp and paper, power station and chemical plant etc.
Prime Features
> More resistant to extrusion
> Increase the pressure handing capabilities.
Technical Data
| Material | 100% Expanded Graphite Yarn | |
| Temperature Range |
-200 up to +555  atmosphere;-200 up to +650 in Steam
|
|
| Process | Rotating | 3 Mpa |
| Reciprocating | 10 Mpa | |
| Valves | 28 Mpa | |
| Shaft Speed | 18m/s in rotary | |
| PH | 0~14 | |
| Density | 1.5 g/cm3 | |